Because this product is wet foam and cure-type always sprinkle water both on a surface before using the product and a foamed surface after using it 

Technical data Basis Polysiloxane Consistancy Stable paste Curing system Moisture curing Skin formation 25 - 30 min Curing speed * (20°C / 65% R.H.) Ca. 2 mm/24h Hardness 35 ± 5 Shore A Density Ca. 1,45 g/ml Elastic recovery (ISO 7389) > 80 % Maximum allowed distortion 25 % Temperature resistance -60 °C → 180 °C Max. tension (DIN 53504) 1,60 N/mm² Elasticity modulus 100% (DIN 53504) 0,60 N/mm² Elongation at break (DIN 53504) Ca. 500 % Application temperature 5 °C → 35 °C (*) these values may vary depending on environmental factors such as temperature, moisture, and type of substrates.
Silirub  is a high performance, low odor,one-component joint and glazing sealants,based on neutral silicone. Silirub  hasbeen developed for weather sealing ofjoints in the façadeDSSOLFDWLR

Base Polysiloxane Consistency Paste Curing System Moisture Cure Skin formation (20°C/65% R.H.) Ca. 7 min. Curing Rate (20°C/65% R.H.) Ca. 2 mm/24h Hardness (DIN 53505) 17 ± 5 Shore A Specific Gravity (DIN 53479) Ca. 0,95 g/ml Temperature Resistance -60°C to +120°C Elastical Recovery (ISO 7389) > 80 % Maximum allowed Distortion 20 % Elasticity Modulus 100 % (DIN 53504) 0,25 N/mm² Maximum Tension (DIN 53504) 1,25 N/mm² Elongation at Break (DIN 53504) >800 % GENERAL PURPOSE - GP is a high-quality, elastical one-component joint sealant based on silicones.
Characteristics: - Very easy application - Permanent clear, UV-resistant - Stays elastic after curing - Very good adhesion on many materials - Typical acetic smell - General sealing for automotive applications